mig aluminum welding wires

mig aluminum welding wires
Made in China by an OEM supplier, this aluminum welding wires benefits from a steady supply chain, responsive communication, local technical support, manageable costs, and adaptable delivery schedules to suit various project needs.

Key attributes:

diameter: 1.2mm 1.6mm 2.0mm 2.4mm 3.2mm

flux content: International Standard

material: al

melting point: 2700

customized support: OEM, ODM, OBM

weight: 7.26kg/plastic spool

place of origin: Hebei, China

model number: aws a5.10 er5356 GB SAL5356

brand name: naidi

application: Sports equipment, factories, shipbuilding,

Material: Aluminum / Aluminum Alloy

Product name: aluminum welding wire ESAB aws a5.10 er5356 1.2mm supply

Color: white-grey

Standard: AWS db iso

OEM: Accept OEM

Packing: 7.26kg/plastic spool

Shield gas: argon

Feature: Very good in marine atmosphere

Spool materials: Plastic Spoo L(Black)

Yield strength: 132MPa

Packaging and delivery:

Selling Units: Single item

Lead time:

Quantity (kilograms)1 - 500> 500

Lead time (days)              7To be negotiated

Customization options:

Customized logo (Min. order: 500 kilograms)

Customized packaging (Min. order: 500 kilograms)

Graphic customization (Min. order: 500 kilograms)

Product Description:

Aws Er5356

GB SAL5356

Introduction

Is magnesium 5% and a small amount of titanium grain refinement of the aluminum-magnesium alloy wires, with good corrosion resistance, thermal cracking resistance, high strength, good forging. Weld anodized after the white that can provide a good color for the welded joints, is a versatile wide range of welding consumables.

Uses: aluminum aluminum (> = 3% mg) alloy argon arc welding of the most basic filler metal, in the aluminum silicon magnesium, aluminum zinc alloy welding and aluminum-magnesium alloy casting welding is also used, such as locomotive , Chemical pressure vessels, bicycles, aluminum skateboards and other sports equipment, ordnance production, shipbuilding, aviation and other industries

Chemical composition:

Mg 4.5-5.5%

Mn<0.8%

Cr 0.05-0.20%

Ti 0.06-0.20%

Al bal.

Physical Characteristics (Approximate):

Melting temperature 575-633℃ 

Portion 2.65(kg/dm3) 

Conductivity 29(%acs) 

heat diffusivity 120(W/m.k) 

linear expansibility 24.1(10-6/k 20-100℃) 

Mechanical properties of weld joint(as reference):

Tensile of strength 250-300(mpa) 

Yield of strength 110-140(mpa) 

Elongation15-25(%) 

Note

1.Aluminum and silicon wire although there is a strong crack resistance, but poor plasticity so after the need for plastic deformation of the joints, it should avoid the use of aluminum silicon wire.

2. Welding should be strictly removed before welding the edge of the oxide and oil.

3. Welding is the use of pad can be dragged Ronghua metal to ensure the formation of the weld

 Diameter MIG:  0.8mm,1.0mm,  1.2mm,  1.6mm

FAQ

Q: are your trading company or manufacturer?

A:we are factory

Q:how long is your delivery time:

A:Generally it's 7-15 days if the goods are in stock,or it's 15-20days if goods are not in stock,it depends on quantity.

Q:Do you provide free sample?it's free or extra?

A:yes,we offer free sample,but don't pay the cost of freight.

Q:what is your payment term?

A:payment<=1000usd,100% in="" advance.payment="">1000usd ,30%TT in advance,balance before shippment.

If you have another question, pls feel free to contact us as below: