wear resistant flux cored welding wires

Wear resistant flux cored welding wires is a common chromium molybdenum type flux cored wire for CO2 gas protection. Welding arc stability, slag easy. Produced in China, Wear resistant flux cored welding wires is backed by a stable supply chain, quick response to customer needs, local technical support, cost control, and flexible delivery schedules to match equipment maintenance and production requirements.

Use:

Applicable to surfacing various wear parts of the surface, such as gears, dredging bucket, mining machinery and other

wear parts. All kinds of shaft and bearing repair.

Deposited metal Chemical composition (%) (Protective gas: CO2)

Chemical Composition (Guarantee Value):

C ≤0.50

Cr ≤2.50

Mo -

v -

s -

Surfacing layer hardness: HRC≥40°

Reference current (DC +)

Wire size φ1.2  φ1.4  φ1.6 mm, Welding current 220 A, Welding voltage 26 V

Key attributes:

diameter: 1.2mm 1.4mm 1.6mm

flux content: Standerd

material: flux cored welding wires

melting point: International Standard

customized support: OEM, ODM, OBM

weight: 15kg 25kg 250kg 300kg

place of origin: Hebei, China

model number: d172

brand name: Naidi

application: surfacing various wear parts of the surface

warranty: 3 years

Product name: wearproof abrasion resistant welding mig wires roll d172

Packing: 15kg/plastic spool 25kg/coil 250kg 300kg/drum

Model: d172 chromium molybdenum type flux cored wires

Trade Term: FOB CIF exw

Advantage: Welding arc stability, slag easy

Color: bright finish

OEM: Accept OEM

application: gears, dredging bucket, mining machinery

hrc: ≥40 °

Protective gas: CO2

Packaging and delivery:

Selling Units: Single item

Single package size: 37X37X26 cm

Single gross weight: 17.000 kg

Lead time:

Quantity 1 - 500 kilograms Lead time 7 days

Quantity > 500 kilograms Lead time To be negotiated

Precautions:

1. Welding work should be done degreasing, rust treatment.

2. Welding, the gas flow is generally 20 ~ 25L / min.

3. When the flux-cored wire is welded, the dry elongation should be 15 ~ 25mm.

4. Should be preheated to about 300 ℃ before welding large workpiece.

5. The humidity of the welding stock should be kept at less than 60%.

6. Non-vacuum packaging wire storage time should not be more than six months, vacuum packaging wires storage time